Fayyaz, Abdolali and Varahram, Nasser and Davami, Parviz (2017) An investigation on the surface austempering of ductile cast iron. Jurnal Kejuruteraan, 29 (1). pp. 9-12. ISSN 0128-0198

[img]
Preview
PDF
1MB

Official URL: http://www.ukm.my/jkukm/in-press-volume-292017/

Abstract

This research presents surface austempering of ductile cast iron. Surface of pearlitic ductile cast iron samples were austenitised and heated to 810 and 850°C and held at these temperatures for 90 and 105 sec and then austempered at a temperature of 325°C for 60 and 90 min. The microstructure of samples was evaluated by optical microscopy. The hardness profile in polished cross section was also determined. In addition, the depth of austmpered layer was measured. The result indicated that temperature and time of austenitisation intensely effect on surface austempering process. The test results also revealed that the hardness of austempered layer increase when the austenitising temperature and time increase. After surface austempering of ductile cast iron samples, the highest hardness achieved 450 HV in austempered surface-layer. The highest depth of austempered layer 1.7 mm was obtained.

Item Type:Article
Keywords:Austempered ductile iron; Surface hardening; Hardness; Microstructure; Austenitisation
Journal:Jurnal Kejuruteraan
ID Code:11650
Deposited By: ms aida -
Deposited On:17 May 2018 06:34
Last Modified:17 May 2018 06:34

Repository Staff Only: item control page