Effect of metal chloride pre-cursor on the structure of Yb-Doped Ba(Ce, Zr)O3 ceramics electrolyte: a comparative study with different metal salts

Osman, N. and Yaakob, M.H. and Talib, I.A. (2014) Effect of metal chloride pre-cursor on the structure of Yb-Doped Ba(Ce, Zr)O3 ceramics electrolyte: a comparative study with different metal salts. Sains Malaysiana, 43 (9). pp. 1429-1432. ISSN 0126-6039

[img]
Preview
PDF
724kB

Official URL: http://www.ukm.my/jsm/

Abstract

This paper discusses the effect of a metal chloride pre-cursor on the phase formation of Yb-doped Ba(Ce, Zr)O3 solid electrolyte derived from a sol-gel method via acetate and chloride salts. The use of metal chloride as a pre-cursor showed the increased in thermal decomposition temperature (Ttd≈1360oC) compared to the metal nitrate pre-cursor (Ttd≈1280oC) and (b) leading to the formation of impurity phases. At calcination temperature of 1500oC, the sample prepared from metal chloride did not form a single-phase of Ba(Ce, Zr)O3. Impurity phases of BaCl2, BaCO3 and (Ce, Zr)O2 were detected in the sample as proven by XRD result. A high purity compound at relatively lower temperature (T=1400oC) was only obtained for the sample that prepared from metal nitrate compared to acetate and chloride (T>1500oC) and carbonate and oxide (T=1500oC) pre-cursors.

Item Type:Article
Keywords:Ceramics; perovskites; thermal properties; X-ray technique
Journal:Sains Malaysiana
ID Code:7680
Deposited By: ms aida -
Deposited On:06 Oct 2014 08:30
Last Modified:14 Dec 2016 06:44

Repository Staff Only: item control page